Synthetic rubbers
Application: The rubbers of the general purposes used for
the production of tires and different rubber
goods replacing natural rubber in production
of medical articles, colored rubber shoes,
rubber articles for the food industry etc.
Perfectly combined with other types of
rubbers ( SKD, BSK etc. )
BK - 1675
Mooney viscosity MB 1 - 8 ( 125 C )
Mooney viscosity spread inside a batch, max.
Insaturation, % mol.
Ash content, % max.
Weight loss at drying, % max.
Antioxidant content, %
Agidol - 2
or Irganox 1010
|
46-56
8
1.40 - 1.80
0.4
0.3
0.05-0.20
0.02 - 0.08
|
Packing in 30 +/- 1 kg briquettes wrapped up in PE
film put into 1 MT wooden crates or containers.
Loading capacity 23.6 MT net per 40` FCL
Country Of Origin Russian Federation
SKI-3, SKI-3S
Property
Mooney Viscosity MB 1 - 4 at 100 °C
Mooney viscosity spread inside the batch, max.
Ash content , % max.
Weight loss at drying, % max.
Antioxidant content, %
DFFD
or VTS
or Diaphen 13
or NQ-2246 ( Agidol - 2 ) |
SKI-3
65 - 85
+/-4
0.5
0.6
0.15 - 0.3
0.4 - 0.7
0.3 - 0.5
- |
SKI-3S
61 - 84
+/-4
0.35
1.2
-
-
-
0.2 - 0.6 |
SBR-1502
Mooney viscosity MB 1 - 4 ( 100 C )
Mooney viscosity spread inside a batch, % max.
Tensile strength, MPa min.
Elongation at break, % min.
Rebound elasticity, % min.
Ash content, % max.
Weight loss at drying, % max.
Antioxidant content, %
Mass fraction of Cu, % max.
Mass fraction of Fe, % max.
Mass fraction of organic acids, %
Mass fraction of organic acids soaps, % max.
Mass fraction of bound Styrene, %
|
48-58
5
27
560
38
0.8
0.4
1 - 2
0.000015
0.004
5.2 - 7.2
0.25
22 - 25
|
Packing in 30 +/- 1 kg briquettes wrapped up in PE
film put into 450 kg net crates
Loading capacity 23.6 MT net per 40` FCL
Country Of Origin Russian Federation
SKD-2 (BR-1220)
Mooney viscosity MB 1 - 4 ( 100 C )
Mooney viscosity spread inside a batch, % max.
Mass fraction of CIS-1,4 units, %
Tensile strength, MPa min.
Elongation at break, % min.
Modulus at 300 % elongation, MPa min.
Residual deformation after break, % max.
Rebound elasticity, % min.
Ash content, % max.
Weight loss at drying, % max.
Antioxidant Agidol - 2 content, %
Mass fraction of Cu, % max.
Mass fraction of Fe, % max.
|
40 - 50
6
87 - 90
19.1
480
19.1
12
51
0.3
0.3
0.05 - 0.20
0.0002
0.0004
|
Packing in 30 +/- 1 kg briquettes wrapped up in PE
film put into 1 MT wooden crates or containers.
Loading capacity 23.6 MT net per 40` FCL
Country Of Origin Russian Federation
SKN-26M
Mooney viscosity MB 1 - 4 ( 100 C )
Mooney viscosity spread inside a batch, max.
Hardness, N
Tensile strenght, MPa min.
Elongation at break, % min.
Vulcanizate mass variation in Isooctantoluene, %max.
Ash content, % max.
Weight loss at drying, % max.
Antioxidant content, %
- Diaphene
- Agidol
Mass fraction of Cu, % max.
Mass fraction of Fe, % max.
Mass fraction of organic acids, %
Mass fraction of organic acids soaps, % max.
Mass fraction of bound Nitrile of Acrylic Acid, %
|
48 - 58 / 70 - 90
5
5.8 - 8.3 /17.2 - 21.5
27.5
625
34
0.6
1
0.2 - 0.3
0.05 - 0.10
0.000015
0.004
6.5
0.4
27 - 30
|
Packing in 30 +/- 1 kg briquettes wrapped up in PE
film put into 450 kg net crates.
Loading capacity 23.6 MT net per 40` FCL
43.2 MT net per r/r box-car
Country Of Origin Russian Federation
|
|